Het OWA, het open archief van het Waterbouwkundig Laboratorium heeft tot doel alle vrij toegankelijke onderzoeksresultaten van dit instituut in digitale vorm aan te bieden. Op die manier wil het de zichtbaarheid, verspreiding en gebruik van deze onderzoeksresultaten, alsook de wetenschappelijke communicatie maximaal bevorderen.
Dit archief wordt uitgebouwd en beheerd volgens de principes van de Open Access Movement, en het daaruit ontstane Open Archives Initiative.
Basisinformatie over ‘Open Access to scholarly information'.
| one publication added to basket [243400] |
Influence of cracks on the service life of concrete structures in a marine environment
Audenaert, K.; Marsavina, L.; De Schutter, G. (2009). Influence of cracks on the service life of concrete structures in a marine environment, in: Marsavina, L. (Ed.) Advances in Strength of Materials. Key Engineering Materials, 399: pp. 153-160. https://dx.doi.org/10.4028/www.scientific.net/KEM.399.153
In: Marsavina, L. (Ed.) (2009). Advances in Strength of Materials. Key Engineering Materials, 399. Trans Tech Publications ltd: Stafa-Zürich. ISBN 978-0-87849-351-7. 230 pp., meer
In: Key Engineering Materials. Trans Tech Publications: Ädermannsdorf. ISSN 0252-1059; e-ISSN 1013-9826, meer
|  |
| Beschikbaar in | Auteurs |
|
Documenttype: Congresbijdrage
|
| Auteurs | | Top |
- Audenaert, K., meer
- Marsavina, L.
- De Schutter, G., meer
|
|
|
| Abstract |
Chloride initiated reinforcement corrosion is the main durability problem for concrete structures in a marine environment. If the chlorides reach the reinforcement steel, it will depassivate and start to corrode in presence of air and water. Since the corrosion products have a larger volume than the initial products, concrete stresses are induced, leading to spalling and degradation of the concrete structures. If cracks, caused by early drying, thermal effects, shrinkage movements or overstress, are present in the concrete, the penetration of chlorides is much faster compared to uncracked concrete. In this way, the corrosion process is initiated earlier and the service life is decreasing drastically. In order to study the influence of existing cracks in concrete structures on the penetration of chlorides a test program was set up at the Magnel Laboratory for Concrete Research of Ghent University, Belgium in cooperation with the "Politehnica" University of Timisoara, Romania. The first part of the test program consists of concrete specimens with artificial cracks. The chloride penetration into the concrete was realised with a non-steady state migration test and modelled with the finite element method COSMOS/FFE Thermal software. Based on the experimental and numerical results, a crack influencing factor was determined. With this factor, the resulting service life of the cracked concrete construction is determined and compared with the original service life. |